SAE-AISI 4340M Steel vs. C95400 Bronze
SAE-AISI 4340M steel belongs to the iron alloys classification, while C95400 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 4340M steel and the bottom bar is C95400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 710 | |
| 160 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 6.0 | |
| 8.1 to 16 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 2340 | |
| 600 to 710 |
| Tensile Strength: Yield (Proof), MPa | 1240 | |
| 240 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 230 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1040 |
| Melting Onset (Solidus), °C | 1400 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Conductivity, W/m-K | 38 | |
| 59 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.8 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.9 | |
| 27 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 3.2 |
| Embodied Energy, MJ/kg | 26 | |
| 53 |
| Embodied Water, L/kg | 55 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 48 to 75 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 4120 | |
| 250 to 560 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 84 | |
| 20 to 24 |
| Strength to Weight: Bending, points | 51 | |
| 19 to 22 |
| Thermal Diffusivity, mm2/s | 10 | |
| 16 |
| Thermal Shock Resistance, points | 70 | |
| 21 to 25 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10 to 11.5 |
| Carbon (C), % | 0.38 to 0.43 | |
| 0 |
| Chromium (Cr), % | 0.7 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 83 to 87 |
| Iron (Fe), % | 93.3 to 94.8 | |
| 3.0 to 5.0 |
| Manganese (Mn), % | 0.65 to 0.9 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.35 to 0.45 | |
| 0 |
| Nickel (Ni), % | 1.7 to 2.0 | |
| 0 to 1.5 |
| Phosphorus (P), % | 0 to 0.012 | |
| 0 |
| Silicon (Si), % | 1.5 to 1.8 | |
| 0 |
| Sulfur (S), % | 0 to 0.012 | |
| 0 |
| Vanadium (V), % | 0.050 to 0.1 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |