SAE-AISI 4419 Steel vs. S30600 Stainless Steel

Both SAE-AISI 4419 steel and S30600 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4419 steel and the bottom bar is S30600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
45
Fatigue Strength, MPa 190
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 310
430
Tensile Strength: Ultimate (UTS), MPa 490
610
Tensile Strength: Yield (Proof), MPa 270
270

Thermal Properties

Latent Heat of Fusion, J/g 250
350
Maximum Temperature: Mechanical, °C 410
950
Melting Completion (Liquidus), °C 1470
1380
Melting Onset (Solidus), °C 1420
1330
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 50
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
19
Density, g/cm3 7.9
7.6
Embodied Carbon, kg CO2/kg material 1.5
3.6
Embodied Energy, MJ/kg 20
51
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 97
220
Resilience: Unit (Modulus of Resilience), kJ/m3 190
190
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 13
3.7
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0.18 to 0.23
0 to 0.018
Chromium (Cr), % 0
17 to 18.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 98.1 to 98.8
58.9 to 65.3
Manganese (Mn), % 0.45 to 0.65
0 to 2.0
Molybdenum (Mo), % 0.45 to 0.6
0 to 0.2
Nickel (Ni), % 0
14 to 15.5
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0.15 to 0.35
3.7 to 4.3
Sulfur (S), % 0 to 0.040
0 to 0.020