SAE-AISI 4615 Steel vs. EN 1.0446 Cast Steel

Both SAE-AISI 4615 steel and EN 1.0446 cast steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4615 steel and the bottom bar is EN 1.0446 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
25
Fatigue Strength, MPa 260
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 480
530
Tensile Strength: Yield (Proof), MPa 350
270

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 47
53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2
1.7
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 22
18
Embodied Water, L/kg 50
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 320
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
19
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0.13 to 0.18
0
Iron (Fe), % 96.4 to 97.4
99.935 to 100
Manganese (Mn), % 0.45 to 0.65
0
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 1.7 to 2.0
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.040
0 to 0.030