SAE-AISI 4626 Steel vs. EN 1.3960 Stainless Steel

Both SAE-AISI 4626 steel and EN 1.3960 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4626 steel and the bottom bar is EN 1.3960 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
34
Fatigue Strength, MPa 240
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 500
590
Tensile Strength: Yield (Proof), MPa 330
270

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
970
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
15
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
21
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
4.1
Embodied Energy, MJ/kg 20
57
Embodied Water, L/kg 48
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
170
Resilience: Unit (Modulus of Resilience), kJ/m3 290
190
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 12
3.9
Thermal Shock Resistance, points 15
17

Alloy Composition

Carbon (C), % 0.24 to 0.29
0 to 0.030
Chromium (Cr), % 0
16.5 to 18.5
Iron (Fe), % 97.4 to 98.3
60.2 to 67.9
Manganese (Mn), % 0.45 to 0.65
0 to 2.0
Molybdenum (Mo), % 0.15 to 0.25
2.5 to 3.0
Nickel (Ni), % 0.7 to 1.0
13 to 15
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.020