SAE-AISI 4718 Steel vs. SAE-AISI 1118 Steel

Both SAE-AISI 4718 steel and SAE-AISI 1118 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI 4718 steel and the bottom bar is SAE-AISI 1118 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 24
13
Fatigue Strength, MPa 270
260
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 330
300
Tensile Strength: Ultimate (UTS), MPa 510
490
Tensile Strength: Yield (Proof), MPa 370
410

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
52
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
19
Embodied Water, L/kg 51
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
61
Resilience: Unit (Modulus of Resilience), kJ/m3 360
450
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
17
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 10
14
Thermal Shock Resistance, points 17
15

Alloy Composition

Carbon (C), % 0.16 to 0.21
0.14 to 0.2
Chromium (Cr), % 0.35 to 0.55
0
Iron (Fe), % 96.3 to 97.4
98 to 98.5
Manganese (Mn), % 0.7 to 0.9
1.3 to 1.6
Molybdenum (Mo), % 0.3 to 0.4
0
Nickel (Ni), % 0.9 to 1.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.040
0.080 to 0.13