SAE-AISI 4815 Steel vs. SAE-AISI 6118 Steel

Both SAE-AISI 4815 steel and SAE-AISI 6118 steel are iron alloys. Both are furnished in the annealed condition. They have a very high 96% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI 4815 steel and the bottom bar is SAE-AISI 6118 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
23
Fatigue Strength, MPa 260
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 350
300
Tensile Strength: Ultimate (UTS), MPa 550
470
Tensile Strength: Yield (Proof), MPa 370
290

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
45
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 7.6
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.7
Embodied Energy, MJ/kg 24
23
Embodied Water, L/kg 53
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
93
Resilience: Unit (Modulus of Resilience), kJ/m3 360
220
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
17
Strength to Weight: Bending, points 19
17
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 18
14

Alloy Composition

Carbon (C), % 0.13 to 0.18
0.16 to 0.21
Chromium (Cr), % 0
0.5 to 0.7
Iron (Fe), % 94.7 to 95.9
97.8 to 98.6
Manganese (Mn), % 0.4 to 0.6
0.5 to 0.7
Molybdenum (Mo), % 0.2 to 0.3
0
Nickel (Ni), % 3.3 to 3.8
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.040
0 to 0.040
Vanadium (V), % 0
0.1 to 0.15