SAE-AISI 50B50 Steel vs. 443.0 Aluminum

SAE-AISI 50B50 steel belongs to the iron alloys classification, while 443.0 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is SAE-AISI 50B50 steel and the bottom bar is 443.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
41
Elastic (Young's, Tensile) Modulus, GPa 190
71
Elongation at Break, % 22
5.6
Fatigue Strength, MPa 260
55
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
27
Shear Strength, MPa 370
96
Tensile Strength: Ultimate (UTS), MPa 590
150
Tensile Strength: Yield (Proof), MPa 370
65

Thermal Properties

Latent Heat of Fusion, J/g 250
470
Maximum Temperature: Mechanical, °C 410
180
Melting Completion (Liquidus), °C 1460
630
Melting Onset (Solidus), °C 1410
580
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 45
150
Thermal Expansion, µm/m-K 13
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
38
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
130

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.4
8.0
Embodied Energy, MJ/kg 19
150
Embodied Water, L/kg 48
1120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
6.9
Resilience: Unit (Modulus of Resilience), kJ/m3 370
30
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
52
Strength to Weight: Axial, points 21
16
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 12
61
Thermal Shock Resistance, points 17
6.9

Alloy Composition

Aluminum (Al), % 0
90.7 to 95.5
Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.48 to 0.53
0
Chromium (Cr), % 0.4 to 0.6
0 to 0.25
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 97.4 to 98.2
0 to 0.8
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0.75 to 1.0
0 to 0.5
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0.15 to 0.35
4.5 to 6.0
Sulfur (S), % 0 to 0.040
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.35