SAE-AISI 50B50 Steel vs. SAE-AISI 1132 Steel
Both SAE-AISI 50B50 steel and SAE-AISI 1132 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 50B50 steel and the bottom bar is SAE-AISI 1132 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 180 | |
190 to 210 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 22 | |
14 to 18 |
Fatigue Strength, MPa | 260 | |
240 to 380 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
73 |
Shear Strength, MPa | 370 | |
400 to 440 |
Tensile Strength: Ultimate (UTS), MPa | 590 | |
640 to 720 |
Tensile Strength: Yield (Proof), MPa | 370 | |
350 to 590 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Maximum Temperature: Mechanical, °C | 410 | |
400 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1410 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 45 | |
51 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
7.1 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
8.2 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.0 | |
1.9 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.4 |
Embodied Energy, MJ/kg | 19 | |
19 |
Embodied Water, L/kg | 48 | |
48 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
93 to 97 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
330 to 940 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 21 | |
23 to 25 |
Strength to Weight: Bending, points | 20 | |
21 to 23 |
Thermal Diffusivity, mm2/s | 12 | |
14 |
Thermal Shock Resistance, points | 17 | |
19 to 22 |
Alloy Composition
Boron (B), % | 0.00050 to 0.0030 | |
0 |
Carbon (C), % | 0.48 to 0.53 | |
0.24 to 0.34 |
Chromium (Cr), % | 0.4 to 0.6 | |
0 |
Iron (Fe), % | 97.4 to 98.2 | |
97.8 to 98.3 |
Manganese (Mn), % | 0.75 to 1.0 | |
1.4 to 1.7 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.040 |
Silicon (Si), % | 0.15 to 0.35 | |
0 |
Sulfur (S), % | 0 to 0.040 | |
0.080 to 0.13 |