SAE-AISI 50B60 Steel vs. AISI 420 Stainless Steel

Both SAE-AISI 50B60 steel and AISI 420 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 50B60 steel and the bottom bar is AISI 420 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 190
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 20
8.0 to 15
Fatigue Strength, MPa 240 to 330
220 to 670
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Shear Strength, MPa 380
420 to 1010
Tensile Strength: Ultimate (UTS), MPa 610 to 630
690 to 1720
Tensile Strength: Yield (Proof), MPa 350 to 530
380 to 1310

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 410
620
Melting Completion (Liquidus), °C 1450
1510
Melting Onset (Solidus), °C 1410
1450
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
27
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
7.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 19
28
Embodied Water, L/kg 48
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 100
88 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 750
380 to 4410
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22 to 23
25 to 62
Strength to Weight: Bending, points 20 to 21
22 to 41
Thermal Diffusivity, mm2/s 12
7.3
Thermal Shock Resistance, points 20
25 to 62

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.56 to 0.64
0.15 to 0.4
Chromium (Cr), % 0.4 to 0.6
12 to 14
Iron (Fe), % 97.3 to 98.1
82.3 to 87.9
Manganese (Mn), % 0.75 to 1.0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 0.75
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030

Comparable Variants