SAE-AISI 50B60 Steel vs. ASTM A372 Grade F Steel
Both SAE-AISI 50B60 steel and ASTM A372 grade F steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is SAE-AISI 50B60 steel and the bottom bar is ASTM A372 grade F steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 190 | |
| 200 to 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 12 to 20 | |
| 20 to 22 |
| Fatigue Strength, MPa | 240 to 330 | |
| 310 to 380 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 380 | |
| 410 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 610 to 630 | |
| 650 to 910 |
| Tensile Strength: Yield (Proof), MPa | 350 to 530 | |
| 430 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 420 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 44 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 2.4 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 19 | |
| 20 |
| Embodied Water, L/kg | 48 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 100 | |
| 130 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 750 | |
| 500 to 810 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 23 | |
| 23 to 32 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 21 to 27 |
| Thermal Diffusivity, mm2/s | 12 | |
| 12 |
| Thermal Shock Resistance, points | 20 | |
| 19 to 27 |
Alloy Composition
| Boron (B), % | 0.00050 to 0.0030 | |
| 0 |
| Carbon (C), % | 0.56 to 0.64 | |
| 0.3 to 0.4 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 0.8 to 1.2 |
| Iron (Fe), % | 97.3 to 98.1 | |
| 96.8 to 97.9 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.015 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.010 |