SAE-AISI 50B60 Steel vs. Grade TDSiCrV Steel

Both SAE-AISI 50B60 steel and grade TDSiCrV steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 50B60 steel and the bottom bar is grade TDSiCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 190
630
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
80
Tensile Strength: Ultimate (UTS), MPa 610 to 630
2100

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 410
420
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
47
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
2.3
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 19
26
Embodied Water, L/kg 48
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22 to 23
75
Strength to Weight: Bending, points 20 to 21
47
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 20
63

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.56 to 0.64
0.5 to 0.7
Chromium (Cr), % 0.4 to 0.6
0.5 to 1.0
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 97.3 to 98.1
96.1 to 97.8
Manganese (Mn), % 0.75 to 1.0
0.4 to 0.9
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0.15 to 0.35
1.2 to 1.7
Sulfur (S), % 0 to 0.040
0 to 0.020
Vanadium (V), % 0
0.1 to 0.25