SAE-AISI 50B60 Steel vs. N08811 Stainless Steel
Both SAE-AISI 50B60 steel and N08811 stainless steel are iron alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 50B60 steel and the bottom bar is N08811 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 20 | |
| 33 |
| Fatigue Strength, MPa | 240 to 330 | |
| 150 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 77 |
| Shear Strength, MPa | 380 | |
| 340 |
| Tensile Strength: Ultimate (UTS), MPa | 610 to 630 | |
| 510 |
| Tensile Strength: Yield (Proof), MPa | 350 to 530 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1390 |
| Melting Onset (Solidus), °C | 1410 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 45 | |
| 12 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 30 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 5.3 |
| Embodied Energy, MJ/kg | 19 | |
| 76 |
| Embodied Water, L/kg | 48 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 100 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 750 | |
| 94 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 23 | |
| 18 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 3.0 |
| Thermal Shock Resistance, points | 20 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.15 to 0.6 |
| Boron (B), % | 0.00050 to 0.0030 | |
| 0 |
| Carbon (C), % | 0.56 to 0.64 | |
| 0.060 to 0.1 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 19 to 23 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 97.3 to 98.1 | |
| 39.5 to 50.6 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 30 to 35 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.6 |