SAE-AISI 5130 Steel vs. EN 1.0558 Cast Steel

Both SAE-AISI 5130 steel and EN 1.0558 cast steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5130 steel and the bottom bar is EN 1.0558 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 22
18
Fatigue Strength, MPa 230 to 330
230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 500 to 640
640
Tensile Strength: Yield (Proof), MPa 330 to 530
340

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 50
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 74 to 98
99
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 750
300
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 23
22
Strength to Weight: Bending, points 18 to 21
21
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 16 to 20
20

Alloy Composition

Carbon (C), % 0.28 to 0.33
0
Chromium (Cr), % 0.8 to 1.1
0
Iron (Fe), % 97.2 to 98.1
99.935 to 100
Manganese (Mn), % 0.7 to 0.9
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.040
0 to 0.030