SAE-AISI 5130 Steel vs. EN 1.0580 Steel

Both SAE-AISI 5130 steel and EN 1.0580 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI 5130 steel and the bottom bar is EN 1.0580 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 190
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 22
5.6 to 25
Fatigue Strength, MPa 230 to 330
210 to 270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 310 to 390
340 to 360
Tensile Strength: Ultimate (UTS), MPa 500 to 640
540 to 620
Tensile Strength: Yield (Proof), MPa 330 to 530
290 to 450

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 50
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 74 to 98
31 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 750
230 to 540
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 23
19 to 22
Strength to Weight: Bending, points 18 to 21
19 to 21
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 16 to 20
17 to 20

Alloy Composition

Carbon (C), % 0.28 to 0.33
0 to 0.22
Chromium (Cr), % 0.8 to 1.1
0
Iron (Fe), % 97.2 to 98.1
97.5 to 100
Manganese (Mn), % 0.7 to 0.9
0 to 1.6
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 0.55
Sulfur (S), % 0 to 0.040
0 to 0.045

Comparable Variants