SAE-AISI 5130 Steel vs. EN 1.4595 Stainless Steel

Both SAE-AISI 5130 steel and EN 1.4595 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5130 steel and the bottom bar is EN 1.4595 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 12 to 22
29
Fatigue Strength, MPa 230 to 330
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 310 to 390
310
Tensile Strength: Ultimate (UTS), MPa 500 to 640
470
Tensile Strength: Yield (Proof), MPa 330 to 530
250

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 420
810
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
30
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
10
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.4
Embodied Energy, MJ/kg 19
34
Embodied Water, L/kg 50
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 74 to 98
110
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 750
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 23
17
Strength to Weight: Bending, points 18 to 21
17
Thermal Diffusivity, mm2/s 12
8.1
Thermal Shock Resistance, points 16 to 20
17

Alloy Composition

Carbon (C), % 0.28 to 0.33
0 to 0.020
Chromium (Cr), % 0.8 to 1.1
14 to 16
Iron (Fe), % 97.2 to 98.1
81.3 to 85.8
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Niobium (Nb), % 0
0.2 to 0.6
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015