SAE-AISI 5132 Steel vs. EN 1.4000 Stainless Steel

Both SAE-AISI 5132 steel and EN 1.4000 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5132 steel and the bottom bar is EN 1.4000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
22
Fatigue Strength, MPa 230
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 320
320
Tensile Strength: Ultimate (UTS), MPa 510
500
Tensile Strength: Yield (Proof), MPa 330
260

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 420
760
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
30
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 9.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 19
27
Embodied Water, L/kg 50
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
91
Resilience: Unit (Modulus of Resilience), kJ/m3 290
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 13
8.1
Thermal Shock Resistance, points 16
18

Alloy Composition

Carbon (C), % 0.3 to 0.35
0 to 0.080
Chromium (Cr), % 0.75 to 1.0
12 to 14
Iron (Fe), % 97.4 to 98.2
83.9 to 88
Manganese (Mn), % 0.6 to 0.8
0 to 1.0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015