SAE-AISI 5132 Steel vs. EN 1.7033 Steel

Both SAE-AISI 5132 steel and EN 1.7033 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5132 steel and the bottom bar is EN 1.7033 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
150 to 240
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 510
500 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
45
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 9.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 50
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
18 to 61
Strength to Weight: Bending, points 18
18 to 41
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 16
15 to 50

Alloy Composition

Carbon (C), % 0.3 to 0.35
0.3 to 0.37
Chromium (Cr), % 0.75 to 1.0
0.9 to 1.2
Iron (Fe), % 97.4 to 98.2
97.1 to 98.2
Manganese (Mn), % 0.6 to 0.8
0.6 to 0.9
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.035