SAE-AISI 5140 Steel vs. EN 1.4612 Stainless Steel

Both SAE-AISI 5140 steel and EN 1.4612 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5140 steel and the bottom bar is EN 1.4612 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 29
11
Fatigue Strength, MPa 220 to 570
860 to 950
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 360 to 600
1010 to 1110
Tensile Strength: Ultimate (UTS), MPa 560 to 970
1690 to 1850
Tensile Strength: Yield (Proof), MPa 290 to 840
1570 to 1730

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 420
790
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
11

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
16
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.6
Embodied Energy, MJ/kg 19
50
Embodied Water, L/kg 49
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 76 to 180
190 to 210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20 to 34
60 to 65
Strength to Weight: Bending, points 19 to 28
40 to 43
Thermal Shock Resistance, points 16 to 29
58 to 63

Alloy Composition

Aluminum (Al), % 0
1.4 to 1.8
Carbon (C), % 0.38 to 0.43
0 to 0.015
Chromium (Cr), % 0.7 to 0.9
11 to 12.5
Iron (Fe), % 97.3 to 98.1
71.5 to 75.5
Manganese (Mn), % 0.7 to 0.9
0 to 0.1
Molybdenum (Mo), % 0
1.8 to 2.3
Nickel (Ni), % 0
10.2 to 11.3
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.035
0 to 0.010
Silicon (Si), % 0.15 to 0.35
0 to 0.1
Sulfur (S), % 0 to 0.040
0 to 0.0050
Titanium (Ti), % 0
0.2 to 0.5

Comparable Variants