SAE-AISI 5140 Steel vs. Grade CX2MW Nickel
SAE-AISI 5140 steel belongs to the iron alloys classification, while grade CX2MW nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 5140 steel and the bottom bar is grade CX2MW nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 12 to 29 | |
| 34 |
| Fatigue Strength, MPa | 220 to 570 | |
| 260 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 560 to 970 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 290 to 840 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 980 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1550 |
| Melting Onset (Solidus), °C | 1420 | |
| 1490 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Conductivity, W/m-K | 45 | |
| 10 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 1.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 65 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 12 |
| Embodied Energy, MJ/kg | 19 | |
| 170 |
| Embodied Water, L/kg | 49 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 76 to 180 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 1880 | |
| 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 20 to 34 | |
| 19 |
| Strength to Weight: Bending, points | 19 to 28 | |
| 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 2.7 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0.38 to 0.43 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0.7 to 0.9 | |
| 20 to 22.5 |
| Iron (Fe), % | 97.3 to 98.1 | |
| 2.0 to 6.0 |
| Manganese (Mn), % | 0.7 to 0.9 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 12.5 to 14.5 |
| Nickel (Ni), % | 0 | |
| 51.3 to 63 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.025 |
| Tungsten (W), % | 0 | |
| 2.5 to 3.5 |
| Vanadium (V), % | 0 | |
| 0 to 0.35 |