SAE-AISI 5140 Steel vs. C19500 Copper
SAE-AISI 5140 steel belongs to the iron alloys classification, while C19500 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 5140 steel and the bottom bar is C19500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 12 to 29 | |
| 2.3 to 38 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 44 |
| Shear Strength, MPa | 360 to 600 | |
| 260 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 560 to 970 | |
| 380 to 640 |
| Tensile Strength: Yield (Proof), MPa | 290 to 840 | |
| 120 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1090 |
| Melting Onset (Solidus), °C | 1420 | |
| 1090 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 45 | |
| 200 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 50 to 56 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 50 to 57 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 31 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 19 | |
| 42 |
| Embodied Water, L/kg | 49 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 76 to 180 | |
| 14 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 1880 | |
| 59 to 1530 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 20 to 34 | |
| 12 to 20 |
| Strength to Weight: Bending, points | 19 to 28 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 58 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 13 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Carbon (C), % | 0.38 to 0.43 | |
| 0 |
| Chromium (Cr), % | 0.7 to 0.9 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 0.3 to 1.3 |
| Copper (Cu), % | 0 | |
| 94.9 to 98.6 |
| Iron (Fe), % | 97.3 to 98.1 | |
| 1.0 to 2.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.7 to 0.9 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0.010 to 0.35 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.1 to 1.0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.2 |