SAE-AISI 5145 Steel vs. EN 1.8062 Steel
Both SAE-AISI 5145 steel and EN 1.8062 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 5145 steel and the bottom bar is EN 1.8062 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 170 | |
200 to 510 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
72 |
Tensile Strength: Ultimate (UTS), MPa | 560 | |
660 to 1910 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
270 |
Maximum Temperature: Mechanical, °C | 420 | |
420 |
Melting Completion (Liquidus), °C | 1460 | |
1440 |
Melting Onset (Solidus), °C | 1410 | |
1400 |
Specific Heat Capacity, J/kg-K | 470 | |
480 |
Thermal Conductivity, W/m-K | 47 | |
43 |
Thermal Expansion, µm/m-K | 12 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
7.4 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
8.6 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.1 | |
2.4 |
Density, g/cm3 | 7.8 | |
7.7 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.5 |
Embodied Energy, MJ/kg | 19 | |
20 |
Embodied Water, L/kg | 49 | |
49 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 20 | |
24 to 69 |
Strength to Weight: Bending, points | 19 | |
22 to 44 |
Thermal Diffusivity, mm2/s | 13 | |
12 |
Thermal Shock Resistance, points | 17 | |
20 to 57 |
Alloy Composition
Carbon (C), % | 0.43 to 0.48 | |
0.42 to 0.5 |
Chromium (Cr), % | 0.7 to 0.9 | |
0.5 to 0.8 |
Iron (Fe), % | 97.3 to 98 | |
95.9 to 97.1 |
Manganese (Mn), % | 0.7 to 0.9 | |
0.5 to 0.8 |
Molybdenum (Mo), % | 0 | |
0.2 to 0.3 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.025 |
Silicon (Si), % | 0.15 to 0.35 | |
1.3 to 1.7 |
Sulfur (S), % | 0 to 0.040 | |
0 to 0.025 |