SAE-AISI 5147 Steel vs. EN 1.6217 Steel

Both SAE-AISI 5147 steel and EN 1.6217 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5147 steel and the bottom bar is EN 1.6217 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
24
Fatigue Strength, MPa 250
280
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 370
350
Tensile Strength: Ultimate (UTS), MPa 600
550
Tensile Strength: Yield (Proof), MPa 360
390

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 46
50
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 19
21
Embodied Water, L/kg 50
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 360
410
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 18
16

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.050
Carbon (C), % 0.46 to 0.51
0 to 0.16
Chromium (Cr), % 0.85 to 1.2
0
Iron (Fe), % 97 to 97.8
96.6 to 99
Manganese (Mn), % 0.7 to 1.0
0.85 to 1.7
Nickel (Ni), % 0
0.15 to 0.85
Niobium (Nb), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.040
0 to 0.010
Vanadium (V), % 0
0 to 0.050