SAE-AISI 5160 Steel vs. EN 1.3940 Stainless Steel

Both SAE-AISI 5160 steel and EN 1.3940 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 5160 steel and the bottom bar is EN 1.3940 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 12 to 18
34
Fatigue Strength, MPa 180 to 650
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 660 to 1150
540
Tensile Strength: Yield (Proof), MPa 280 to 1010
240

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 420
930
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 43
15
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.3
Embodied Energy, MJ/kg 19
47
Embodied Water, L/kg 50
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 73 to 160
150
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 2700
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 41
19
Strength to Weight: Bending, points 22 to 31
19
Thermal Diffusivity, mm2/s 12
4.1
Thermal Shock Resistance, points 19 to 34
16

Alloy Composition

Carbon (C), % 0.56 to 0.61
0 to 0.030
Chromium (Cr), % 0.7 to 0.9
16.5 to 18.5
Iron (Fe), % 97.1 to 97.8
64.2 to 71.4
Manganese (Mn), % 0.75 to 1.0
0 to 2.0
Nickel (Ni), % 0
12 to 14
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.020