SAE-AISI 51B60 Steel vs. AWS E316LMn

Both SAE-AISI 51B60 steel and AWS E316LMn are iron alloys. They have 55% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 51B60 steel and the bottom bar is AWS E316LMn.

SAE-AISI 51B60 (G51601) Boron Steel AWS E316LMn (W31622) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		12 to 21
Elongation at Break, %		23

Poisson's Ratio		0.29
Poisson's Ratio		0.28

Shear Modulus, GPa		73
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		660
Tensile Strength: Ultimate (UTS), MPa		620

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1450
Melting Completion (Liquidus), °C		1420

Melting Onset (Solidus), °C		1410
Melting Onset (Solidus), °C		1370

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		2.1
Base Metal Price, % relative		24

Density, g/cm³		7.8
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		1.4
Embodied Carbon, kg CO₂/kg material		4.6

Embodied Energy, MJ/kg		19
Embodied Energy, MJ/kg		64

Embodied Water, L/kg		49
Embodied Water, L/kg		180

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		23
Strength to Weight: Axial, points		22

Strength to Weight: Bending, points		22
Strength to Weight: Bending, points		20

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		15

Alloy Composition

Boron (B), %		0.00050 to 0.0030
Boron (B), %		0

Carbon (C), %		0.56 to 0.64
Carbon (C), %		0 to 0.040

Chromium (Cr), %		0.7 to 0.9
Chromium (Cr), %		18 to 21

Copper (Cu), %		0
Copper (Cu), %		0 to 0.75

Iron (Fe), %		97 to 97.8
Iron (Fe), %		47.5 to 59.4

Manganese (Mn), %		0.75 to 1.0
Manganese (Mn), %		5.0 to 8.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		2.5 to 3.5

Nickel (Ni), %		0
Nickel (Ni), %		15 to 18

Nitrogen (N), %		0
Nitrogen (N), %		0.1 to 0.25

Phosphorus (P), %		0 to 0.035
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0.15 to 0.35
Silicon (Si), %		0 to 0.9

Sulfur (S), %		0 to 0.040
Sulfur (S), %		0 to 0.030