SAE-AISI 51B60 Steel vs. EN 1.0449 Cast Steel

Both SAE-AISI 51B60 steel and EN 1.0449 cast steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 51B60 steel and the bottom bar is EN 1.0449 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 21
28
Fatigue Strength, MPa 280 to 340
170
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 660
460
Tensile Strength: Yield (Proof), MPa 400 to 550
220

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 49
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 73 to 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 420 to 800
130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
16
Strength to Weight: Bending, points 22
17
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 19
14

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.56 to 0.64
0 to 0.18
Chromium (Cr), % 0.7 to 0.9
0
Iron (Fe), % 97 to 97.8
98 to 100
Manganese (Mn), % 0.75 to 1.0
0 to 1.2
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.025