SAE-AISI 51B60 Steel vs. EN 1.5521 Steel
Both SAE-AISI 51B60 steel and EN 1.5521 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 51B60 steel and the bottom bar is EN 1.5521 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 200 | |
130 to 180 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 12 to 21 | |
11 to 21 |
Fatigue Strength, MPa | 280 to 340 | |
210 to 310 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
73 |
Shear Strength, MPa | 390 to 420 | |
310 to 360 |
Tensile Strength: Ultimate (UTS), MPa | 660 | |
430 to 1390 |
Tensile Strength: Yield (Proof), MPa | 400 to 550 | |
300 to 490 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Maximum Temperature: Mechanical, °C | 420 | |
400 |
Melting Completion (Liquidus), °C | 1450 | |
1460 |
Melting Onset (Solidus), °C | 1410 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 43 | |
51 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
7.1 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
8.1 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.1 | |
1.9 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.4 |
Embodied Energy, MJ/kg | 19 | |
19 |
Embodied Water, L/kg | 49 | |
47 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 to 120 | |
44 to 230 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 to 800 | |
250 to 630 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 23 | |
15 to 49 |
Strength to Weight: Bending, points | 22 | |
16 to 35 |
Thermal Diffusivity, mm2/s | 12 | |
14 |
Thermal Shock Resistance, points | 19 | |
13 to 41 |
Alloy Composition
Boron (B), % | 0.00050 to 0.0030 | |
0.00080 to 0.0050 |
Carbon (C), % | 0.56 to 0.64 | |
0.16 to 0.2 |
Chromium (Cr), % | 0.7 to 0.9 | |
0 |
Copper (Cu), % | 0 | |
0 to 0.25 |
Iron (Fe), % | 97 to 97.8 | |
98 to 98.9 |
Manganese (Mn), % | 0.75 to 1.0 | |
0.9 to 1.2 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.025 |
Silicon (Si), % | 0.15 to 0.35 | |
0 to 0.3 |
Sulfur (S), % | 0 to 0.040 | |
0 to 0.025 |