SAE-AISI 51B60 Steel vs. Monel R-405
SAE-AISI 51B60 steel belongs to the iron alloys classification, while Monel R-405 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 51B60 steel and the bottom bar is Monel R-405.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 160 |
| Elongation at Break, % | 12 to 21 | |
| 9.1 to 39 |
| Fatigue Strength, MPa | 280 to 340 | |
| 210 to 250 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 62 |
| Shear Strength, MPa | 390 to 420 | |
| 350 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 540 to 630 |
| Tensile Strength: Yield (Proof), MPa | 400 to 550 | |
| 190 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 900 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1350 |
| Melting Onset (Solidus), °C | 1410 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Conductivity, W/m-K | 43 | |
| 23 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 50 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 7.9 |
| Embodied Energy, MJ/kg | 19 | |
| 110 |
| Embodied Water, L/kg | 49 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 to 120 | |
| 49 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 to 800 | |
| 120 to 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 10 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 23 | |
| 17 to 20 |
| Strength to Weight: Bending, points | 22 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 5.9 |
| Thermal Shock Resistance, points | 19 | |
| 17 to 20 |
Alloy Composition
| Boron (B), % | 0.00050 to 0.0030 | |
| 0 |
| Carbon (C), % | 0.56 to 0.64 | |
| 0 to 0.3 |
| Chromium (Cr), % | 0.7 to 0.9 | |
| 0 |
| Copper (Cu), % | 0 | |
| 28 to 34 |
| Iron (Fe), % | 97 to 97.8 | |
| 0 to 2.5 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 63 to 72 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.040 | |
| 0.025 to 0.060 |