SAE-AISI 51B60 Steel vs. SAE-AISI 1043 Steel

Both SAE-AISI 51B60 steel and SAE-AISI 1043 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 51B60 steel and the bottom bar is SAE-AISI 1043 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
190 to 200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 21
13 to 18
Fatigue Strength, MPa 280 to 340
230 to 390
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 390 to 420
400 to 430
Tensile Strength: Ultimate (UTS), MPa 660
650 to 710
Tensile Strength: Yield (Proof), MPa 400 to 550
350 to 600

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 49
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 73 to 120
87 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 420 to 800
320 to 980
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
23 to 25
Strength to Weight: Bending, points 22
21 to 22
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 19
21 to 22

Alloy Composition

Boron (B), % 0.00050 to 0.0030
0
Carbon (C), % 0.56 to 0.64
0.4 to 0.47
Chromium (Cr), % 0.7 to 0.9
0
Iron (Fe), % 97 to 97.8
98.4 to 98.9
Manganese (Mn), % 0.75 to 1.0
0.7 to 1.0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.040
0 to 0.050