SAE-AISI 52100 Steel vs. EN 1.4021 Stainless Steel
Both SAE-AISI 52100 steel and EN 1.4021 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 52100 steel and the bottom bar is EN 1.4021 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 10 to 20 | |
| 11 to 17 |
| Fatigue Strength, MPa | 250 to 340 | |
| 240 to 380 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 76 |
| Shear Strength, MPa | 370 to 420 | |
| 390 to 530 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 2010 | |
| 630 to 880 |
| Tensile Strength: Yield (Proof), MPa | 360 to 560 | |
| 390 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 760 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 47 | |
| 30 |
| Thermal Expansion, µm/m-K | 12 to 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 7.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.9 |
| Embodied Energy, MJ/kg | 20 | |
| 27 |
| Embodied Water, L/kg | 51 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 54 to 310 | |
| 88 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 350 to 840 | |
| 400 to 1160 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 72 | |
| 23 to 31 |
| Strength to Weight: Bending, points | 20 to 45 | |
| 21 to 26 |
| Thermal Diffusivity, mm2/s | 13 | |
| 8.1 |
| Thermal Shock Resistance, points | 19 to 61 | |
| 22 to 31 |
Alloy Composition
| Carbon (C), % | 0.93 to 1.1 | |
| 0.16 to 0.25 |
| Chromium (Cr), % | 1.4 to 1.6 | |
| 12 to 14 |
| Iron (Fe), % | 96.5 to 97.3 | |
| 83.2 to 87.8 |
| Manganese (Mn), % | 0.25 to 0.45 | |
| 0 to 1.5 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |