SAE-AISI 6150 Steel vs. EN 1.4410 Stainless Steel

Both SAE-AISI 6150 steel and EN 1.4410 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 6150 steel and the bottom bar is EN 1.4410 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 350
260
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 15 to 23
24
Fatigue Strength, MPa 300 to 750
410
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
81
Shear Strength, MPa 400 to 730
540
Tensile Strength: Ultimate (UTS), MPa 630 to 1200
850
Tensile Strength: Yield (Proof), MPa 420 to 1160
600

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 12 to 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
20
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.0
4.0
Embodied Energy, MJ/kg 28
56
Embodied Water, L/kg 51
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 180
180
Resilience: Unit (Modulus of Resilience), kJ/m3 460 to 3590
880
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22 to 43
30
Strength to Weight: Bending, points 21 to 32
26
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 20 to 38
23

Alloy Composition

Carbon (C), % 0.48 to 0.53
0 to 0.030
Chromium (Cr), % 0.8 to 1.1
24 to 26
Iron (Fe), % 96.7 to 97.7
58.1 to 66.8
Manganese (Mn), % 0.7 to 0.9
0 to 2.0
Molybdenum (Mo), % 0
3.0 to 4.5
Nickel (Ni), % 0
6.0 to 8.0
Nitrogen (N), % 0
0.24 to 0.35
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015
Vanadium (V), % 0.15 to 0.3
0