SAE-AISI 8615 Steel vs. ASTM Grade HC Steel

Both SAE-AISI 8615 steel and ASTM grade HC steel are iron alloys. They have 70% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 8615 steel and the bottom bar is ASTM grade HC steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 25
6.0
Fatigue Strength, MPa 220
96
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 480
430
Tensile Strength: Yield (Proof), MPa 310
200

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 39
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
14
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.5
2.8
Embodied Energy, MJ/kg 20
40
Embodied Water, L/kg 50
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
21
Resilience: Unit (Modulus of Resilience), kJ/m3 250
95
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 17
16
Strength to Weight: Bending, points 17
16
Thermal Diffusivity, mm2/s 10
4.5
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0.13 to 0.18
0 to 0.5
Chromium (Cr), % 0.4 to 0.6
26 to 30
Iron (Fe), % 96.9 to 98.1
61.9 to 74
Manganese (Mn), % 0.7 to 0.9
0 to 1.0
Molybdenum (Mo), % 0.15 to 0.25
0 to 0.5
Nickel (Ni), % 0.4 to 0.7
0 to 4.0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 2.0
Sulfur (S), % 0 to 0.040
0 to 0.040