SAE-AISI 8642 Steel vs. 1100 Aluminum

SAE-AISI 8642 steel belongs to the iron alloys classification, while 1100 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is SAE-AISI 8642 steel and the bottom bar is 1100 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
69
Elongation at Break, % 23
1.1 to 32
Fatigue Strength, MPa 270
32 to 71
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Shear Strength, MPa 370
54 to 95
Tensile Strength: Ultimate (UTS), MPa 580
86 to 170
Tensile Strength: Yield (Proof), MPa 380
28 to 150

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 410
180
Melting Completion (Liquidus), °C 1460
660
Melting Onset (Solidus), °C 1420
640
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 39
220
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
59
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
190

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
9.0
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.5
8.2
Embodied Energy, MJ/kg 20
150
Embodied Water, L/kg 50
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
0.76 to 52
Resilience: Unit (Modulus of Resilience), kJ/m3 390
5.7 to 170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 20
8.7 to 17
Strength to Weight: Bending, points 20
16 to 25
Thermal Diffusivity, mm2/s 10
90
Thermal Shock Resistance, points 17
3.7 to 7.4

Alloy Composition

Aluminum (Al), % 0
99 to 99.95
Carbon (C), % 0.4 to 0.45
0
Chromium (Cr), % 0.4 to 0.6
0
Copper (Cu), % 0
0.050 to 0.2
Iron (Fe), % 96.6 to 97.8
0 to 1.0
Manganese (Mn), % 0.75 to 1.0
0 to 0.050
Molybdenum (Mo), % 0.15 to 0.25
0
Nickel (Ni), % 0.4 to 0.7
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15