SAE-AISI 8740 Steel vs. 333.0 Aluminum
SAE-AISI 8740 steel belongs to the iron alloys classification, while 333.0 aluminum belongs to the aluminum alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is SAE-AISI 8740 steel and the bottom bar is 333.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 200 | |
| 90 to 110 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 73 |
| Elongation at Break, % | 11 to 23 | |
| 1.0 to 2.0 |
| Fatigue Strength, MPa | 270 to 350 | |
| 83 to 100 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 28 |
| Shear Strength, MPa | 370 to 400 | |
| 190 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 670 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 380 to 570 | |
| 130 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 520 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 590 |
| Melting Onset (Solidus), °C | 1420 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 880 |
| Thermal Conductivity, W/m-K | 39 | |
| 100 to 140 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 26 to 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 83 to 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 10 |
| Density, g/cm3 | 7.8 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 7.6 |
| Embodied Energy, MJ/kg | 20 | |
| 140 |
| Embodied Water, L/kg | 50 | |
| 1040 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 120 | |
| 2.1 to 4.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 390 to 850 | |
| 120 to 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 49 |
| Strength to Weight: Axial, points | 20 to 24 | |
| 22 to 27 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 29 to 34 |
| Thermal Diffusivity, mm2/s | 10 | |
| 42 to 57 |
| Thermal Shock Resistance, points | 17 to 20 | |
| 11 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 81.8 to 89 |
| Carbon (C), % | 0.38 to 0.43 | |
| 0 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 0 |
| Copper (Cu), % | 0 | |
| 3.0 to 4.0 |
| Iron (Fe), % | 96.5 to 97.7 | |
| 0 to 1.0 |
| Magnesium (Mg), % | 0 | |
| 0.050 to 0.5 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.2 to 0.3 | |
| 0 |
| Nickel (Ni), % | 0.4 to 0.7 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 8.0 to 10 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |