SAE-AISI 9254 Steel vs. EN 1.4318 Stainless Steel

Both SAE-AISI 9254 steel and EN 1.4318 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 9254 steel and the bottom bar is EN 1.4318 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
230
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
44
Fatigue Strength, MPa 280
340
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Shear Strength, MPa 410
520
Tensile Strength: Ultimate (UTS), MPa 660
740
Tensile Strength: Yield (Proof), MPa 410
380

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Mechanical, °C 410
910
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
13
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.8
Embodied Energy, MJ/kg 20
39
Embodied Water, L/kg 49
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
280
Resilience: Unit (Modulus of Resilience), kJ/m3 450
360
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
27
Strength to Weight: Bending, points 22
23
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 20
17

Alloy Composition

Carbon (C), % 0.51 to 0.59
0 to 0.030
Chromium (Cr), % 0.6 to 0.8
16.5 to 18.5
Iron (Fe), % 96.1 to 97.1
70.2 to 77.4
Manganese (Mn), % 0.6 to 0.8
0 to 2.0
Nickel (Ni), % 0
6.0 to 8.0
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 1.2 to 1.6
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015