SAE-AISI 9255 Steel vs. ACI-ASTM CA15M Steel

Both SAE-AISI 9255 steel and ACI-ASTM CA15M steel are iron alloys. They have 86% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 9255 steel and the bottom bar is ACI-ASTM CA15M steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
20
Fatigue Strength, MPa 270
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Tensile Strength: Ultimate (UTS), MPa 680
690
Tensile Strength: Yield (Proof), MPa 390
510

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Mechanical, °C 400
760
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 46
27
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
7.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.1
Embodied Energy, MJ/kg 20
29
Embodied Water, L/kg 46
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
130
Resilience: Unit (Modulus of Resilience), kJ/m3 400
670
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
25
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 13
7.2
Thermal Shock Resistance, points 21
25

Alloy Composition

Carbon (C), % 0.51 to 0.59
0 to 0.15
Chromium (Cr), % 0
11.5 to 14
Iron (Fe), % 96.2 to 97
82.1 to 88.4
Manganese (Mn), % 0.7 to 1.0
0 to 1.0
Molybdenum (Mo), % 0
0.15 to 1.0
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 1.8 to 2.2
0 to 0.65
Sulfur (S), % 0 to 0.040
0 to 0.040