SAE-AISI 9255 Steel vs. EN 1.5510 Steel

Both SAE-AISI 9255 steel and EN 1.5510 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 9255 steel and the bottom bar is EN 1.5510 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
130 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
11 to 21
Fatigue Strength, MPa 270
220 to 330
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 430
310 to 380
Tensile Strength: Ultimate (UTS), MPa 680
450 to 1600
Tensile Strength: Yield (Proof), MPa 390
310 to 520

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 46
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 20
19
Embodied Water, L/kg 46
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
46 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 400
260 to 710
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
16 to 57
Strength to Weight: Bending, points 22
17 to 39
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 21
13 to 47

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.51 to 0.59
0.25 to 0.3
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 96.2 to 97
97.9 to 99.149
Manganese (Mn), % 0.7 to 1.0
0.6 to 0.9
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 1.8 to 2.2
0 to 0.3
Sulfur (S), % 0 to 0.040
0 to 0.025