SAE-AISI 9255 Steel vs. EN 1.7375 Steel

Both SAE-AISI 9255 steel and EN 1.7375 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 9255 steel and the bottom bar is EN 1.7375 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
20
Fatigue Strength, MPa 270
270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
74
Shear Strength, MPa 430
380
Tensile Strength: Ultimate (UTS), MPa 680
620
Tensile Strength: Yield (Proof), MPa 390
400

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 400
460
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 46
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
3.9
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 20
23
Embodied Water, L/kg 46
59

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 400
420
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 21
18

Alloy Composition

Aluminum (Al), % 0
0.010 to 0.040
Carbon (C), % 0.51 to 0.59
0.1 to 0.15
Chromium (Cr), % 0
2.0 to 2.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 96.2 to 97
94.5 to 96.7
Manganese (Mn), % 0.7 to 1.0
0.3 to 0.8
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 1.8 to 2.2
0 to 0.3
Sulfur (S), % 0 to 0.040
0 to 0.010