SAE-AISI 94B30 Steel vs. N06058 Nickel
SAE-AISI 94B30 steel belongs to the iron alloys classification, while N06058 nickel belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 94B30 steel and the bottom bar is N06058 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 25 | |
| 45 |
| Fatigue Strength, MPa | 220 | |
| 350 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 86 |
| Shear Strength, MPa | 320 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 300 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 980 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1540 |
| Melting Onset (Solidus), °C | 1420 | |
| 1490 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 420 |
| Thermal Conductivity, W/m-K | 39 | |
| 9.8 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 70 |
| Density, g/cm3 | 7.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 13 |
| Embodied Energy, MJ/kg | 20 | |
| 170 |
| Embodied Water, L/kg | 49 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 18 | |
| 27 |
| Strength to Weight: Bending, points | 18 | |
| 23 |
| Thermal Diffusivity, mm2/s | 10 | |
| 2.6 |
| Thermal Shock Resistance, points | 15 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.4 |
| Boron (B), % | 0.00050 to 0.0030 | |
| 0 |
| Carbon (C), % | 0.28 to 0.33 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0.3 to 0.5 | |
| 20 to 23 |
| Cobalt (Co), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 97 to 98.1 | |
| 0 to 1.5 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.080 to 0.15 | |
| 19 to 21 |
| Nickel (Ni), % | 0.3 to 0.6 | |
| 52.2 to 61 |
| Nitrogen (N), % | 0 | |
| 0.020 to 0.15 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.015 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.3 |