SAE-AISI A10 Steel vs. EN 1.4841 Stainless Steel

Both SAE-AISI A10 steel and EN 1.4841 stainless steel are iron alloys. They have 56% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI A10 steel and the bottom bar is EN 1.4841 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
78
Tensile Strength: Ultimate (UTS), MPa 810 to 2040
650

Thermal Properties

Latent Heat of Fusion, J/g 270
330
Melting Completion (Liquidus), °C 1440
1380
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 40
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 9.0
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 5.0
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.1
4.3
Embodied Energy, MJ/kg 27
62
Embodied Water, L/kg 56
190

Common Calculations

PREN (Pitting Resistance) 5.1
26
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29 to 73
23
Strength to Weight: Bending, points 25 to 46
21
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 27 to 68
15

Alloy Composition

Carbon (C), % 1.3 to 1.5
0 to 0.2
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 90.8 to 93.4
47.1 to 55.5
Manganese (Mn), % 1.6 to 2.1
0 to 2.0
Molybdenum (Mo), % 1.3 to 1.8
0
Nickel (Ni), % 1.6 to 2.1
19 to 22
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 1.0 to 1.5
1.5 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.015