SAE-AISI A3 Steel vs. S31277 Stainless Steel
Both SAE-AISI A3 steel and S31277 stainless steel are iron alloys. They have 48% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI A3 steel and the bottom bar is S31277 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 2150 | |
| 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 310 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.0 | |
| 36 |
| Density, g/cm3 | 7.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 6.7 |
| Embodied Energy, MJ/kg | 67 | |
| 90 |
| Embodied Water, L/kg | 78 | |
| 220 |
Common Calculations
| PREN (Pitting Resistance) | 8.9 | |
| 51 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 25 to 77 | |
| 29 |
| Strength to Weight: Bending, points | 23 to 48 | |
| 25 |
| Thermal Shock Resistance, points | 23 to 70 | |
| 19 |
Alloy Composition
| Carbon (C), % | 1.2 to 1.3 | |
| 0 to 0.020 |
| Chromium (Cr), % | 4.8 to 5.5 | |
| 20.5 to 23 |
| Copper (Cu), % | 0 to 0.25 | |
| 0.5 to 1.5 |
| Iron (Fe), % | 88.7 to 92 | |
| 35.5 to 46.2 |
| Manganese (Mn), % | 0.4 to 0.6 | |
| 0 to 3.0 |
| Molybdenum (Mo), % | 0.9 to 1.4 | |
| 6.5 to 8.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 26 to 28 |
| Nitrogen (N), % | 0 | |
| 0.3 to 0.4 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Vanadium (V), % | 0.8 to 1.4 | |
| 0 |