SAE-AISI A7 Steel vs. R60706 Alloy
SAE-AISI A7 steel belongs to the iron alloys classification, while R60706 alloy belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI A7 steel and the bottom bar is R60706 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 2150 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 37 | |
| 17 |
| Thermal Expansion, µm/m-K | 12 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 6.7 |
| Embodied Water, L/kg | 100 | |
| 450 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 29 to 77 | |
| 24 |
| Strength to Weight: Bending, points | 25 to 48 | |
| 23 |
| Thermal Diffusivity, mm2/s | 10 | |
| 9.5 |
| Thermal Shock Resistance, points | 27 to 72 | |
| 67 |
Alloy Composition
| Carbon (C), % | 2.0 to 2.9 | |
| 0 to 0.050 |
| Chromium (Cr), % | 5.0 to 5.8 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 81.4 to 87.7 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 to 0.8 | |
| 0 |
| Molybdenum (Mo), % | 0.9 to 1.4 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 2.0 to 3.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 0.5 to 1.5 | |
| 0 |
| Vanadium (V), % | 3.9 to 5.2 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 91 to 98 |