SAE-AISI A8 Steel vs. AWS E320
Both SAE-AISI A8 steel and AWS E320 are iron alloys. They have 45% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI A8 steel and the bottom bar is AWS E320.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 1920 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1410 |
| Melting Onset (Solidus), °C | 1430 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.5 | |
| 38 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 6.5 |
| Embodied Energy, MJ/kg | 31 | |
| 91 |
| Embodied Water, L/kg | 73 | |
| 220 |
Common Calculations
| PREN (Pitting Resistance) | 12 | |
| 28 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 25 to 68 | |
| 21 |
| Strength to Weight: Bending, points | 22 to 44 | |
| 20 |
| Thermal Shock Resistance, points | 22 to 62 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.5 to 0.6 | |
| 0 to 0.070 |
| Chromium (Cr), % | 4.8 to 5.5 | |
| 19 to 21 |
| Copper (Cu), % | 0 to 0.25 | |
| 3.0 to 4.0 |
| Iron (Fe), % | 88.5 to 91.9 | |
| 31.8 to 43.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.5 to 2.5 |
| Molybdenum (Mo), % | 1.2 to 1.7 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 32 to 36 |
| Niobium (Nb), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.75 to 1.1 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 1.0 to 1.5 | |
| 0 |