SAE-AISI D2 Steel vs. EN 1.4588 Stainless Steel

Both SAE-AISI D2 steel and EN 1.4588 stainless steel are iron alloys. They have 60% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI D2 steel and the bottom bar is EN 1.4588 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 5.0 to 16
34
Fatigue Strength, MPa 310 to 860
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
80
Tensile Strength: Ultimate (UTS), MPa 760 to 2000
540
Tensile Strength: Yield (Proof), MPa 470 to 1510
240

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 31
15
Thermal Expansion, µm/m-K 11
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 5.1
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
33
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 3.4
6.2
Embodied Energy, MJ/kg 50
84
Embodied Water, L/kg 100
200

Common Calculations

PREN (Pitting Resistance) 15
44
Resilience: Ultimate (Unit Rupture Work), MJ/m3 92 to 100
150
Resilience: Unit (Modulus of Resilience), kJ/m3 570 to 5940
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27 to 72
18
Strength to Weight: Bending, points 24 to 46
18
Thermal Diffusivity, mm2/s 8.3
4.0
Thermal Shock Resistance, points 25 to 67
11

Alloy Composition

Carbon (C), % 1.4 to 1.6
0 to 0.020
Chromium (Cr), % 11 to 13
19 to 21
Copper (Cu), % 0 to 0.25
0.5 to 1.5
Iron (Fe), % 81.3 to 86.9
41.2 to 50.4
Manganese (Mn), % 0 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.7 to 1.2
6.0 to 7.0
Nickel (Ni), % 0 to 0.3
24 to 26
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0 to 1.1
0