SAE-AISI D3 Steel vs. ASTM A210 Steel
Both SAE-AISI D3 steel and ASTM A210 steel are iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI D3 steel and the bottom bar is ASTM A210 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 9.8 to 15 | |
| 34 |
| Fatigue Strength, MPa | 310 to 940 | |
| 230 to 250 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Shear Strength, MPa | 470 to 1220 | |
| 320 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 2050 | |
| 470 to 540 |
| Tensile Strength: Yield (Proof), MPa | 480 to 1550 | |
| 290 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1460 to 1470 |
| Melting Onset (Solidus), °C | 1390 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 31 | |
| 52 to 53 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.0 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 | |
| 8.0 to 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 1.8 |
| Density, g/cm3 | 7.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 1.4 |
| Embodied Energy, MJ/kg | 48 | |
| 18 |
| Embodied Water, L/kg | 100 | |
| 45 to 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 97 to 180 | |
| 140 to 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 74 | |
| 17 to 19 |
| Strength to Weight: Bending, points | 24 to 47 | |
| 17 to 19 |
| Thermal Diffusivity, mm2/s | 8.3 | |
| 14 |
| Thermal Shock Resistance, points | 23 to 63 | |
| 15 to 17 |