SAE-AISI D4 Steel vs. Nickel 601
SAE-AISI D4 steel belongs to the iron alloys classification, while nickel 601 belongs to the nickel alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI D4 steel and the bottom bar is nickel 601.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 8.4 to 15 | |
| 10 to 38 |
| Fatigue Strength, MPa | 310 to 920 | |
| 220 to 380 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 76 |
| Shear Strength, MPa | 460 to 1210 | |
| 440 to 530 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 2060 | |
| 660 to 890 |
| Tensile Strength: Yield (Proof), MPa | 470 to 1540 | |
| 290 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1410 |
| Melting Onset (Solidus), °C | 1380 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 31 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.2 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.0 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 49 |
| Density, g/cm3 | 7.7 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 8.0 |
| Embodied Energy, MJ/kg | 49 | |
| 110 |
| Embodied Water, L/kg | 100 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 160 | |
| 86 to 200 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 27 to 75 | |
| 22 to 30 |
| Strength to Weight: Bending, points | 24 to 47 | |
| 20 to 25 |
| Thermal Diffusivity, mm2/s | 8.3 | |
| 2.8 |
| Thermal Shock Resistance, points | 23 to 63 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 1.0 to 1.7 |
| Carbon (C), % | 2.1 to 2.4 | |
| 0 to 0.1 |
| Chromium (Cr), % | 11 to 13 | |
| 21 to 25 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 1.0 |
| Iron (Fe), % | 80.6 to 86.3 | |
| 7.7 to 20 |
| Manganese (Mn), % | 0 to 0.6 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.7 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 58 to 63 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 to 1.0 | |
| 0 |