SAE-AISI D5 Steel vs. EN 1.4303 Stainless Steel

Both SAE-AISI D5 steel and EN 1.4303 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI D5 steel and the bottom bar is EN 1.4303 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 5.4 to 14
13 to 49
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
77
Shear Strength, MPa 470 to 1180
420 to 540
Tensile Strength: Ultimate (UTS), MPa 770 to 2030
590 to 900

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 27
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 4.9
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
17
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.5
3.2
Embodied Energy, MJ/kg 51
46
Embodied Water, L/kg 120
150

Common Calculations

PREN (Pitting Resistance) 15
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28 to 73
21 to 32
Strength to Weight: Bending, points 24 to 46
20 to 26
Thermal Diffusivity, mm2/s 7.4
4.0
Thermal Shock Resistance, points 26 to 67
13 to 20

Alloy Composition

Carbon (C), % 1.4 to 1.6
0 to 0.060
Chromium (Cr), % 11 to 13
17 to 19
Cobalt (Co), % 2.5 to 3.5
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 77.9 to 84.4
64.8 to 72
Manganese (Mn), % 0 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.7 to 1.2
0
Nickel (Ni), % 0 to 0.3
11 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 0 to 1.0
0