SAE-AISI D7 Steel vs. ASTM B817 Type I
SAE-AISI D7 steel belongs to the iron alloys classification, while ASTM B817 type I belongs to the titanium alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI D7 steel and the bottom bar is ASTM B817 type I.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 2120 | |
| 770 to 960 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 410 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1600 |
| Melting Onset (Solidus), °C | 1400 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 560 |
| Thermal Conductivity, W/m-K | 27 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 36 |
| Density, g/cm3 | 7.6 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 38 |
| Embodied Energy, MJ/kg | 180 | |
| 610 |
| Embodied Water, L/kg | 130 | |
| 200 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 35 |
| Strength to Weight: Axial, points | 29 to 78 | |
| 48 to 60 |
| Strength to Weight: Bending, points | 25 to 48 | |
| 42 to 49 |
| Thermal Diffusivity, mm2/s | 7.4 | |
| 2.9 |
| Thermal Shock Resistance, points | 27 to 72 | |
| 54 to 68 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 2.2 to 2.5 | |
| 0 to 0.1 |
| Chlorine (Cl), % | 0 | |
| 0 to 0.2 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 76.6 to 81.9 | |
| 0 to 0.4 |
| Manganese (Mn), % | 0 to 0.6 | |
| 0 |
| Molybdenum (Mo), % | 0.7 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.1 |
| Sodium (Na), % | 0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 87 to 91 |
| Vanadium (V), % | 3.8 to 4.4 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |