SAE-AISI F1 Steel vs. SAE-AISI 1212 Steel
Both SAE-AISI F1 steel and SAE-AISI 1212 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI F1 steel and the bottom bar is SAE-AISI 1212 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 2320 | |
| 440 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 24 | |
| 18 |
| Embodied Water, L/kg | 46 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 82 | |
| 15 to 22 |
| Strength to Weight: Bending, points | 20 to 49 | |
| 16 to 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 19 to 70 | |
| 14 to 20 |
Alloy Composition
| Carbon (C), % | 1.0 to 1.3 | |
| 0 to 0.13 |
| Iron (Fe), % | 95.9 to 98 | |
| 98.5 to 99.07 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.7 to 1.0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0.070 to 0.12 |
| Silicon (Si), % | 0.1 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0.16 to 0.23 |
| Tungsten (W), % | 1.0 to 1.8 | |
| 0 |