SAE-AISI F1 Steel vs. C70600 Copper-nickel
SAE-AISI F1 steel belongs to the iron alloys classification, while C70600 copper-nickel belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI F1 steel and the bottom bar is C70600 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 2320 | |
| 290 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 220 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1150 |
| Melting Onset (Solidus), °C | 1430 | |
| 1100 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 45 | |
| 44 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 9.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 9.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 33 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 3.4 |
| Embodied Energy, MJ/kg | 24 | |
| 51 |
| Embodied Water, L/kg | 46 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 22 to 82 | |
| 9.1 to 18 |
| Strength to Weight: Bending, points | 20 to 49 | |
| 11 to 17 |
| Thermal Diffusivity, mm2/s | 12 | |
| 13 |
| Thermal Shock Resistance, points | 19 to 70 | |
| 9.8 to 19 |
Alloy Composition
| Carbon (C), % | 1.0 to 1.3 | |
| 0 |
| Copper (Cu), % | 0 | |
| 84.7 to 90 |
| Iron (Fe), % | 95.9 to 98 | |
| 1.0 to 1.8 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 9.0 to 11 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.1 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 1.0 to 1.8 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |