SAE-AISI F2 Steel vs. 8011A Aluminum

SAE-AISI F2 steel belongs to the iron alloys classification, while 8011A aluminum belongs to the aluminum alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is SAE-AISI F2 steel and the bottom bar is 8011A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
69
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Tensile Strength: Ultimate (UTS), MPa 710 to 2360
100 to 180

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Melting Completion (Liquidus), °C 1520
650
Melting Onset (Solidus), °C 1470
630
Specific Heat Capacity, J/kg-K 460
900
Thermal Conductivity, W/m-K 42
210
Thermal Expansion, µm/m-K 13
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
56
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
180

Otherwise Unclassified Properties

Base Metal Price, % relative 10
9.0
Density, g/cm3 8.1
2.7
Embodied Carbon, kg CO2/kg material 2.3
8.2
Embodied Energy, MJ/kg 32
150
Embodied Water, L/kg 50
1180

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 24 to 81
11 to 18
Strength to Weight: Bending, points 22 to 49
18 to 26
Thermal Diffusivity, mm2/s 11
86
Thermal Shock Resistance, points 21 to 71
4.6 to 8.1

Alloy Composition

Aluminum (Al), % 0
97.5 to 99.1
Carbon (C), % 1.2 to 1.4
0
Chromium (Cr), % 0.2 to 0.4
0 to 0.1
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 92.6 to 95.4
0.5 to 1.0
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0.1 to 0.5
0 to 0.1
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.1 to 0.5
0.4 to 0.8
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 3.0 to 4.5
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15